| 25CrMo钢高速车轴坯的试制 | |
| 顾家琳 ; 刘淑华 ; 周惠华 ; 潘涛 ; 王玉玲 ; 吴海英 ; 施惠基 ; 汝继来 ; 朱静 ; GU Jialin ; LIU Shuhua ; ZHOU Huihua ; PAN Tao ; WANG Yuling ; WU Haiying ; SHI Huiji ; RU Jilai ; ZHU Jing | |
| 2016-03-30 ; 2016-03-30 | |
| 关键词 | 高速列车 车轴 轴坯 热处理 力学性能 疲劳性能 EWT intrinsic mode fault diagnosis adaptive signal decomposition EMD U270.33 |
| 其他题名 | Trial Production of 25CrMo Steel High Speed Axle Billet |
| 中文摘要 | 为了高速列车车轴制造的国产化,试验研究25CrMo钢高速车轴坯机械性能的影响因素。结果表明:25CrMo钢高速车轴坯的成分和洁净度应符合EN 13261—2009标准对EA4T钢的要求,且合金元素含量偏中上线较好;轴坯要保证具有足够的锻造比;经适当的正火、淬火和回火热处理工艺,可保证得到的轴坯常规力学性能和疲劳性能满足车速200~250km·h-1高速列车车轴的要求,且具有优异的缺口疲劳性能,经热处理工艺获得的材料最优疲劳缺口敏感系数为0.16,远低于EN 13261—2009标准最大的允许值0.63;当25CrMo钢成品轴坯的晶粒尺寸控制在8级以上、且在轴坯最大直径1/2半径处的组织为贝氏体和回火马氏体复相组织时,其具有最佳性能。; In order to localize the manufacture of high speed train axle,the influencing factors on the mechanical properties of 25 CrMo steel axle billet were experimentally studied.The results show that the composition and cleanliness of 25 CrMo steel billet should meet the requirements of EN 13261—2009standard for EA4 Tsteel and the percentage of alloy elements should be in higher or medium level.Enough forging ratio of axle billet is necessary.A further appropriate heat treatment process with normalizing,quenching and tempering can ensure that the conventional mechanical properties and fatigue properties of the obtained axle billet satisfy the requirement for high speed train axle at the speed of 200~250km·h-1.The excellent notch fatigue performance is achieved,and the optimal fatigue notch sensitivity coefficient for the sample through the best heat treatment process is 0.16,which is far lower than the maximum allowable value 0.63 in EN 13261—2009standard.When the grain size of the finished 25 CrMo steel axle billet is controlled at level 8or above,and the microstructure at 1/2radius of the largest diameter of the axle billet is bainite and tempered martensite(dual phase),the optimal mechanical properties are obtained. |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://ir.lib.tsinghua.edu.cn/ir/item.do?handle=123456789/141778]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 顾家琳,刘淑华,周惠华,等. 25CrMo钢高速车轴坯的试制[J],2016, 2016. |
| APA | 顾家琳.,刘淑华.,周惠华.,潘涛.,王玉玲.,...&ZHU Jing.(2016).25CrMo钢高速车轴坯的试制.. |
| MLA | 顾家琳,et al."25CrMo钢高速车轴坯的试制".(2016). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论