	Thermoelectric Properties of Ca_3Co_4O_9/Polyaniline Composites
	Bin Zheng ; Yuanhua Lin ; Jinle Lan ; Xiaoping Yang ; Bin Zheng ; Yuanhua Lin ; Jinle Lan ; Xiaoping Yang
	2016-03-30 ; 2016-03-30
关键词	Polyaniline Ca_3Co_4O_9 Thermoelectric Composite TB332
其他题名	Thermoelectric Properties of Ca_3Co_4O_9/Polyaniline Composites
中文摘要	Ca_3Co_4O_9/polyaniline bulk composites have been successfully fabricated by ball-milling and hot-pressing method.Our results indicate that the Seebeck coefficient can be increased nearly by 400%with adding15 wt%Ca_3Co_4O_9 to the polyaniline.The thermal conductivity changes slightly with increasing filler content.The highest figure of merit,ZT can reach 5 �10~(-4) at 329 K for these bulk composites,which is almost 50times larger than that of pure polyaniline,suggesting that the polymer-thermoelectric oxide composites are promising candidates for light-weight,low-cost and non-toxic thermoelectric applications.; Ca_3Co_4O_9/polyaniline bulk composites have been successfully fabricated by ball-milling and hot-pressing method.Our results indicate that the Seebeck coefficient can be increased nearly by 400%with adding15 wt%Ca_3Co_4O_9 to the polyaniline.The thermal conductivity changes slightly with increasing filler content.The highest figure of merit,ZT can reach 5 �10~(-4) at 329 K for these bulk composites,which is almost 50times larger than that of pure polyaniline,suggesting that the polymer-thermoelectric oxide composites are promising candidates for light-weight,low-cost and non-toxic thermoelectric applications.
语种	英语 ; 英语
内容类型	期刊论文
源URL	[http://ir.lib.tsinghua.edu.cn/ir/item.do?handle=123456789/141658]
专题	清华大学
推荐引用方式 GB/T 7714	Bin Zheng,Yuanhua Lin,Jinle Lan,et al. Thermoelectric Properties of Ca_3Co_4O_9/Polyaniline Composites[J],2016, 2016.
APA	Bin Zheng.,Yuanhua Lin.,Jinle Lan.,Xiaoping Yang.,Bin Zheng.,...&Xiaoping Yang.(2016).Thermoelectric Properties of Ca_3Co_4O_9/Polyaniline Composites..
MLA	Bin Zheng,et al."Thermoelectric Properties of Ca_3Co_4O_9/Polyaniline Composites".(2016).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。