Characterization and low-temperature sintering of Ni0.5Zn0.5Fe2O4 nano-powders prepared by refluxing method | |
Yan, Wenxun ; Li, Qiang ; Zhong, Haisheng ; Zhong, Zhifeng | |
2010-10-12 ; 2010-10-12 | |
关键词 | Ni-Zn ferrite Nano-powders Refluxing method CITRATE PRECURSOR METHOD NICKEL-ZINC FERRITES MAGNETIC-PROPERTIES INITIAL PERMEABILITY COMBUSTION PARTICLES Engineering, Chemical |
中文摘要 | The as-prepared Ni0.5Zn0.5Fe2O4 powders fabricated directly from the solution of metal nitrates by the refluxing method were testified by the analysis of XRD, TEM, SAED and HRTEM. XRD pattern indicated that obtained Ni0.5Zn0.5Fe2O4 powders were single phase with spinel structure, TEM analysis showed that the powders with cubic shape were uniform in particle size of about 10-20 nm. Ceramics prepared by the assynthesized Ni0.5Zn0.5Fe2O4 powders sintered at various temperatures between 950 degrees C and 1150 C for 2 h were observed by SEM technique, which indicated that the Ni0.5Zn0.5Fe2O4 ferrites can almost be sintered to theoretic density at 1100 degrees C for 2 h, lower by at least about 200 degrees C compared with those ferrites prepared by the conventional oxide method. The relative magnetic loss tan delta/mu(i) of the ceramic samples sintered at the temperature 1050 degrees C was measured to be of the order of 10(-4)-10(-5) in the frequency range from 1 MHz to 10 MHz, and the threshold frequency of the ferrites was 77.2 MHz. (c) 2008 Published by Elsevier B.V. |
语种 | 英语 ; 英语 |
出版者 | ELSEVIER SCIENCE SA ; LAUSANNE ; PO BOX 564, 1001 LAUSANNE, SWITZERLAND |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/80843] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Yan, Wenxun,Li, Qiang,Zhong, Haisheng,et al. Characterization and low-temperature sintering of Ni0.5Zn0.5Fe2O4 nano-powders prepared by refluxing method[J],2010, 2010. |
APA | Yan, Wenxun,Li, Qiang,Zhong, Haisheng,&Zhong, Zhifeng.(2010).Characterization and low-temperature sintering of Ni0.5Zn0.5Fe2O4 nano-powders prepared by refluxing method.. |
MLA | Yan, Wenxun,et al."Characterization and low-temperature sintering of Ni0.5Zn0.5Fe2O4 nano-powders prepared by refluxing method".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论