Bundled one-dimensional Si/sub 3/N/sub 4/ single-crystalline nanowires are successfully synthesized by pyrolysis of a polymer precursor using Fe as catalyst. The average diameter of the obtained Si/sub 3/N/sub 4/ nanowires is about 200 nm, and the nanowires have perfect single-crystalline structure. Intense photoluminescence was observed centered at 1.83, 2.79, 3.24, and 3.74 eV. The nanowires could be useful in the fabrication of optoelectronic nanodevices and nanocomposites. [All rights reserved Elsevier].
语种
英语
出版者
Editions Scientifiques et Medicales Elsevier
; France
Na Zhu,Zhijian Peng,Chengbiao Wang,et al. Preparation and characterization of bundled one-dimensional Si/sub 3/N/sub 4/ single-crystalline nanowires by catalytic pyrolysis of a polymer precursor[J],2010, 2010.
APA
Na Zhu,Zhijian Peng,Chengbiao Wang,Zhiqiang Fu,&Hezhuo Miao.(2010).Preparation and characterization of bundled one-dimensional Si/sub 3/N/sub 4/ single-crystalline nanowires by catalytic pyrolysis of a polymer precursor..
MLA
Na Zhu,et al."Preparation and characterization of bundled one-dimensional Si/sub 3/N/sub 4/ single-crystalline nanowires by catalytic pyrolysis of a polymer precursor".(2010).
修改评论