Influences of phosphorus pentoxide on sintering behaviors of glass-ceramics from phosphorus slag | |
Cao Jianwei ; Liang Kaiming ; Li Yaohui | |
2010-10-12 ; 2010-10-12 | |
关键词 | Experimental/ glass ceramics particle size phosphorus compounds sintering slag X-ray diffraction/ phosphorus pentoxide sintering glass-ceramics phosphorus slag raw material orthogonal test X-ray diffraction particle size crystalline phase temperature 1000 C to 1050 C P/sub 2/O/sub 5// A8120Q Preparation of glass-based composites A8120E Powder techniques, compaction and sintering/ temperature 1.27315E+03 to 1.32315E+03 K/ P2O5/bin O5/bin P2/bin O/bin P/bin |
中文摘要 | Glass-ceramics were prepared from phosphorus slag as the main raw material by sintering method. The factors influencing the sintering behavior were investigated by orthogonal test and X-ray diffraction. The results show that the dominant factor is sintering temperature, the second is P/sub 2/O/sub 5/ content, the third is the particle size, and the last is the holding time. P/sub 2/O/sub 5/ had a significant effect on the sintering behavior when the other three influential factors were invariable. When the P/sub 2/O/sub 5/ content (mass fraction, the same below) was less than 1.8%, beta -CaSiO/sub 3/ was the main crystalline phase at below 1 000 degrees C and the surface of the glass-ceramics was not smooth. When the P/sub 2/O/sub 5/ content was more than 3.6%, the required sintering temperature was increased to 1 100 degrees C; meanwhile, the required holding time was dramatically prolonged. In this case, Na/sub 2/Ca/sub 2/Si/sub 3/O/sub 9/ became mainly crystalline and the surface of the glass-ceramics was not smooth. As a result, the preferential P/sub 2/O/sub 5/ content was in the range of 1.8%-3.6%, sintering temperature was 1 000-1 050 degrees C, sintering time was 60 min, and glass-ceramics with a smooth and flat surface could be obtained. |
语种 | 中文 |
出版者 | Chinese Ceramic Society ; China |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/78234] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Cao Jianwei,Liang Kaiming,Li Yaohui. Influences of phosphorus pentoxide on sintering behaviors of glass-ceramics from phosphorus slag[J],2010, 2010. |
APA | Cao Jianwei,Liang Kaiming,&Li Yaohui.(2010).Influences of phosphorus pentoxide on sintering behaviors of glass-ceramics from phosphorus slag.. |
MLA | Cao Jianwei,et al."Influences of phosphorus pentoxide on sintering behaviors of glass-ceramics from phosphorus slag".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论