| 中间退火对镁合金板材组织和性能的影响 | |
| 彭伟平 ; 刘腾 ; 何良菊 ; 李培杰 ; 曾攀 ; PENG Wei-ping ; LIU Teng ; HE Liang-ju ; LI Pei-jie ; ZENG Pan | |
| 2010-06-08 ; 2010-06-08 | |
| 关键词 | 镁合金板材 中间退火 微观组织 力学性能 magnesium alloy sheet intermediate annealing microstructure mechanical property TG113.12 TG156.24 |
| 其他题名 | Influence of intermediate annealing on microstructure and mechanical property of magnesium alloy sheet |
| 中文摘要 | 研究AZ31B镁合金轧制道次间不同退火温度和时间对板材微观组织和力学性能的影响,分析了拉伸试样断口形貌。实验结果表明,退火处理后镁合金板材由轧制纤维组织转变为均匀等轴的再结晶组织,退火再结晶的起始温度为200℃;退火后的力学性能得到一定程度的恢复,硬度、屈服强度最大降幅分别为25.4%和37.1%,伸长率最大增幅达31.3%,拉伸断口由解理和韧窝混合断口转变为典型韧性断口。实验得到镁合金中间退火的较佳工艺为:退火温度300~320℃,退火时间60~120min。; The microstructure evolution and mechanical property during intermediate annealing of AZ31B magnesium alloy sheet were investigated by using optical microscope and SEM.The results show that the onset temperature of recrystallization is 200℃.The hardness and the yield strength under the annealed state decrease by 25.4% and 37.1%,respectively,and the elongation increases by 31.3%.The fractography changes from the mixture of cleavage fracture and dimple fracture into entire dimple fracture.The optimal intermediate annealing technology for AZ31 magnesium alloy sheet is annealing at the temperature of 300～320℃ for 30～120 min.; 国家“十五”863国际合作重点项目(2002AADF3306) |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/48498]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 彭伟平,刘腾,何良菊,等. 中间退火对镁合金板材组织和性能的影响[J],2010, 2010. |
| APA | 彭伟平.,刘腾.,何良菊.,李培杰.,曾攀.,...&ZENG Pan.(2010).中间退火对镁合金板材组织和性能的影响.. |
| MLA | 彭伟平,et al."中间退火对镁合金板材组织和性能的影响".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论