耐磨铸造Fe-B-C合金的研究 | |
符寒光 ; 蒋志强 ; FU Hanguang ; JIANG Zhiqiang | |
2010-06-08 ; 2010-06-08 | |
关键词 | 铸造Fe-B-C合金 硼化物 板条马氏体 耐磨性 cast Fe-B-C alloy, boride, lath martensite, abrasion resistance TG136.1 |
其他题名 | A STUDY OF ABRASION RESISTANT CAST Fe-B-C ALLOY |
中文摘要 | 借助光学显微镜、扫描电镜和X射线衍射分析等手段,研究了硼(B)含量>2.0%和碳(C)含量<0.2%的铸造 Fe-B-C合金的凝固组织及热处理后的组织和性能.铸造Fe-B-C合金的凝固组织由Fe2B、铁素体和珠光体组成,硼化物呈网状沿晶界分布.Fe-B-C合金经950℃正火处理后,局部出现断网现象,基体组织全部转变为板条马氏体,硬度大幅度提高, HRC接近60,冲击韧度大于10 J/cm2,动态断裂韧度大于30 MPa·m1/2.在干滑动磨损条件下,Fe-B-C合金的耐磨性优于镍硬白口铸铁和GCr15、Cr12MoV等合金钢,与高铬白口铸铁相当.Fe-B-C合金熔炼简便、铸造性能好,且不含Ni 和MO等昂贵合金元素,具有较低的生产成本.; The solidification structures of cast Fe-B-C alloy containing more than 2.0%B and lower than 0.2%C and the structures and properties of alloy after heat treatment were researched by means of optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), hardness measurements, impact tester and pin abrasion tester. The results show that the solidification structures of cast Fe-B-C alloy consist of boride (Fe2B), pearlite and ferrite, and boride distributes along grain boundary in network form. After normalizing at 950℃, the part broken network of boride in cast Fe-B-C alloy appeared, the matrix all transformed into lath martensite. The hardness of cast Fe-B-C alloy increased obviously and neared to HRC 60, its impact toughness and dynamic fracture toughness exceeded 10 J/cm2 and 30 MPa·m1/2, respectively. In the condition of pin-on-disk wear, cast Fe-B-C alloy showed excellent abrasion resistance. Its abrasion resistance is more excellent than that of Ni-hard white cast iron, GCr15 and Cr12MoV, nears to that of high chromium white cast iron. Cast Fe-B-C alloy has simple melting process and good casting property, does not contain costly nickel and molybdenum elements and so has low production cost.; 中国博士后科学基金资助项目 2004036058 |
语种 | 中文 ; 中文 |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/48177] ![]() |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | 符寒光,蒋志强,FU Hanguang,等. 耐磨铸造Fe-B-C合金的研究[J],2010, 2010. |
APA | 符寒光,蒋志强,FU Hanguang,&JIANG Zhiqiang.(2010).耐磨铸造Fe-B-C合金的研究.. |
MLA | 符寒光,et al."耐磨铸造Fe-B-C合金的研究".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论