| YSZ/Al_2O_3复合陶瓷的制备及性能研究 | |
| 易中周 ; 姚翔华 ; 张举成 ; 刘卫 ; 谢志鹏 ; YI Zhong-zhou ; YAO Xiang-hua ; ZHANG Ju-cheng ; LIU Wei ; XIE Zhi-peng | |
| 2010-05-12 ; 2010-05-12 | |
| 关键词 | YSZ/Al2O3 Zeta电位 流变性能 显微结构 YSZ/Al2O3 Zeta potential rheological behaviors microstructure TQ174 |
| 其他题名 | Preparation and Performance for Zirconia/Alumina Composite Ceramics |
| 中文摘要 | 选用ZrO2(5wt.%Y2O3)和Al2O3为粉体原料,采用溶胶凝胶法制备氧化锆基氧化铝(YSZ/Al2O3)复合陶瓷,研究了悬浮体的Zeta电位、分散性、流变性及其显微结构.结果表明:在pH=9~10附近、选用SD-00为分散剂,加入量为1.0wt.%,粉体最佳配比为70wt.%ZrO2(5wt.%Y2O3)和30wt.%Al2O3,获得固相含量为50Vol.%的悬浮体,制备出了均匀致密、高强度的YSZ/Al2O3复合陶瓷.; Zirconia(5wt.%Y2O3) and Alumina powder are used as theraw material,Zirconia/Alumina Ceramics composite was prepared successfully by gelcasty.Zeta potential,the granulairty distribution,rheological behaviors of the Suspension and The microstructure of green bodies and sintered samples was measured and discussed.The result shown that the YSZ/Al2O3 composite ceramics,which is the 50Vol.% suspension,was prepared at the pH value about 9～10,SD-00 as disperser which addition amount is 1.0wt.%,and the optimum proportion is 70wt.%ZrO2(5wt.%Y2O3) and 30wt.% Al2O3. |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/28948]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 易中周,姚翔华,张举成,等. YSZ/Al_2O_3复合陶瓷的制备及性能研究[J],2010, 2010. |
| APA | 易中周.,姚翔华.,张举成.,刘卫.,谢志鹏.,...&XIE Zhi-peng.(2010).YSZ/Al_2O_3复合陶瓷的制备及性能研究.. |
| MLA | 易中周,et al."YSZ/Al_2O_3复合陶瓷的制备及性能研究".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论