TiO2 photocatalyst high specific surface area: Preparation and hydrogen evolution performance | |
Wang, H ; Wang, XM ; Sun, W ; Mao, ZQ ; Yan, H ; Xie, XF | |
2010-05-10 ; 2010-05-10 | |
关键词 | photocatalysis CTAB TiO2 hydrogen evolution VISIBLE-LIGHT IRRADIATION Chemistry, Inorganic & Nuclear |
中文摘要 | Nanometer sized TiO2 powder with large surface area was synthesized by sol-gel method using tetrabutyl titanate as precursor and hexadecyltrimethylammonium bromide (CTAB) as template. The photocatalyst is characterized on particle size, crystal structure, and surface area by XRD, TEM, BET. The results show that the molar ratio of CTAB to Ti and temperature of calcination have great effect on their particle size and surface area. The photocatalytic activities of hydrogen evolution were compared on samples with different preparation conditions. The results indicate that CTAB obviously improves the hydrogen evolution performance of photocatalytic water splitting, the 0.15-450 sample that the molar ratio of CTAB to Ti is about 0.15 and calcination temperature is 450 degrees C with particle size of 5.73 nm and the specific surface area of 150 m(2.)h(-1) is the best with an average hydrogen evolution rate of 12.5 mL(.)h(-1) in 3 hours. |
语种 | 中文 ; 中文 |
出版者 | CHINESE CHEMICAL SOCIETY ; BEIJING ; C/O DEPT INT AFFAIRS, SECRETARY OF CHEM SOC, PO BOX 2709, BEIJING 100080, PEOPLES R CHINA |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/23054] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Wang, H,Wang, XM,Sun, W,et al. TiO2 photocatalyst high specific surface area: Preparation and hydrogen evolution performance[J],2010, 2010. |
APA | Wang, H,Wang, XM,Sun, W,Mao, ZQ,Yan, H,&Xie, XF.(2010).TiO2 photocatalyst high specific surface area: Preparation and hydrogen evolution performance.. |
MLA | Wang, H,et al."TiO2 photocatalyst high specific surface area: Preparation and hydrogen evolution performance".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论