| Modification of surface mechanical properties of aluminum by high current Mo ion implantation using a MEVVA ion source | |
| Miao, W ; Liu, XT ; Tao, K | |
| 2010-05-10 ; 2010-05-10 | |
| 关键词 | intermetallic compound implantation mechanical property CORROSION BEHAVIOR METALS AL Materials Science, Coatings & Films Physics, Applied |
| 中文摘要 | The surface modification of At by high Current Mo ion implantation using a metal vapor vacuum arc (MEVVA) ion source has been studied. A high aluminum content intermetallic compound Al12Mo was formed using Mo ion implantation into Al with a current density of 64 muA/cm(2) (the temperature of the sample rises to similar to410 degreesC) to a dose of 3 x 10(17) ionS/cm(2) The hardening aluminide layer with a thickness of about 1600 nm was obtained and the hardness of the Al surface increased with increasing the Mo ion dose up to six times larger than that of the unimplanted one. Also, the elastic modulus of the Al surface was increased by the aluminides. (C) 2004 Elsevier B.V All rights reserved. |
| 语种 | 英语 ; 英语 |
| 出版者 | ELSEVIER SCIENCE SA ; LAUSANNE ; PO BOX 564, 1001 LAUSANNE, SWITZERLAND |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/21453]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | Miao, W,Liu, XT,Tao, K. Modification of surface mechanical properties of aluminum by high current Mo ion implantation using a MEVVA ion source[J],2010, 2010. |
| APA | Miao, W,Liu, XT,&Tao, K.(2010).Modification of surface mechanical properties of aluminum by high current Mo ion implantation using a MEVVA ion source.. |
| MLA | Miao, W,et al."Modification of surface mechanical properties of aluminum by high current Mo ion implantation using a MEVVA ion source".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论