Mild corrosion behavior on sulphurized steel surface during friction | |
Wang, HD ; Xu, BS ; Liu, JJ ; Zhuang, DM ; Zhang, XC ; Wei, SC | |
2010-05-07 ; 2010-05-07 | |
关键词 | sulphuration layer FeS friction sulfate radical corrosion TRIBOLOGICAL PROPERTIES SULFIDE LAYER FILMS WEAR DRY Chemistry, Physical Materials Science, Coatings & Films Physics, Applied Physics, Condensed Matter |
中文摘要 | After treatment by low temperature ion sulphuration, the solid lubrication sulphuration layers (FeS films) were produced on the AISI 1045 and stainless steel. A mass of corrosion peeling pits occurred on the worn scars of 1045 steel sulphuration layer after wear test, whereas none of them on the stainless steel one. AFM was used to observe the morphology of sulphuration layer, SEM equipped EDS was utilized to analyze the morphologies and compositions of worn scars. XPS and XRD were employed to detect the valence states of sulphuration layer and its worn scars, as well as the phase structures. The results showed that during friction, under the frictional heat, the sulfate radical with mild corrosion was produced, so that the 1045 steel without any anti-corrosion was corroded in some certain, meanwhile the stainless steel was not corroded depending on its excellent corrosion resistance. (c) 2005 Elsevier B.V. All rights reserved. |
语种 | 英语 ; 英语 |
出版者 | ELSEVIER SCIENCE BV ; AMSTERDAM ; PO BOX 211, 1000 AE AMSTERDAM, NETHERLANDS |
内容类型 | 期刊论文 |
源URL | [http://hdl.handle.net/123456789/15863] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Wang, HD,Xu, BS,Liu, JJ,et al. Mild corrosion behavior on sulphurized steel surface during friction[J],2010, 2010. |
APA | Wang, HD,Xu, BS,Liu, JJ,Zhuang, DM,Zhang, XC,&Wei, SC.(2010).Mild corrosion behavior on sulphurized steel surface during friction.. |
MLA | Wang, HD,et al."Mild corrosion behavior on sulphurized steel surface during friction".(2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论