Fabrication of porous SiC ceramics through a modified gelcasting and solid state sintering | |
Wang, Feng1,2; Yin, Jinwei1; Yao, Dongxu1; Xia, Yongfeng1; Zuo, Kaihui1; Xu, Jiaqiang2; Zeng, Yuping1 | |
刊名 | MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING |
2016-01-27 | |
卷号 | 654页码:292-297 |
关键词 | Porous SiC ceramics Gelcasting Isobam Solid state sintering Starch |
英文摘要 | With starch as pore forming agent, porous silicon carbide (SiC) ceramics were successfully fabricated by gelcasting. A novel and simple gelling system of isobutylene and maleic anhydride (Isobam) can gel in air at room temperature was used. The rheological behaviors of SiC slurries were investigated as a function of starch content. The gelled SiC green bodies were sintered at 2050-2150 degrees C through solid state sintering with B4C and carbon as sintering additives. Porosity of the porous SiC ceramics sintered at 2100 degrees C was well controlled from 34.20% to 42.68% with the starch content increasing from 0 to 20 wt%. With increasing the sintering temperature from 2050 to 2150 degrees C, flexural strength and porosity of porous SiC ceramics with 20 wt% starch varied from 61.0 to 128.0 MPa and 48.1% to 34.2%, respectively. The porous SiC ceramics fabricated with 20 wt% starch addition and sintered at 2100 degrees C were proved to possess excellent thermal shock resistance. The ceramics after water-quenching at 1500 degrees C showed an average flexural strength of 95.8 MPa, which was higher than the strength of samples without quenching. (C) 2015 Elsevier B.V. All rights reserved. |
WOS标题词 | Science & Technology ; Technology |
类目[WOS] | Nanoscience & Nanotechnology ; Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
研究领域[WOS] | Science & Technology - Other Topics ; Materials Science ; Metallurgy & Metallurgical Engineering |
关键词[WOS] | SILICON-CARBIDE CERAMICS ; THERMAL-SHOCK RESISTANCE ; OXIDE ADDITIVES ; MECHANICAL-PROPERTIES ; MASS-SPECTROMETRY ; POWDER BEDS ; MICROSTRUCTURE ; VAPORIZATION ; SIC-AL2O3 ; STRENGTH |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000370111100034 |
内容类型 | 期刊论文 |
源URL | [http://ir.sic.ac.cn/handle/331005/23178] |
专题 | 上海硅酸盐研究所_结构陶瓷与复合材料工程研究中心_期刊论文 |
作者单位 | 1.Chinese Acad Sci, Shanghai Inst Ceram, Shanghai 200050, Peoples R China 2.Shanghai Univ, Dept Chem, Shanghai 200444, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Feng,Yin, Jinwei,Yao, Dongxu,et al. Fabrication of porous SiC ceramics through a modified gelcasting and solid state sintering[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2016,654:292-297. |
APA | Wang, Feng.,Yin, Jinwei.,Yao, Dongxu.,Xia, Yongfeng.,Zuo, Kaihui.,...&Zeng, Yuping.(2016).Fabrication of porous SiC ceramics through a modified gelcasting and solid state sintering.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,654,292-297. |
MLA | Wang, Feng,et al."Fabrication of porous SiC ceramics through a modified gelcasting and solid state sintering".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 654(2016):292-297. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论