Ethanolamine-assisted synthesis of size-controlled indium tin oxide nanoinks for low temperature solution deposited transparent conductive films | |
Chen, Z(陈征); Qin, XC(秦喜超); Zhou, T(周腾); Wu, XZ(吴馨洲); Shao, SS(邵霜霜); Xie, ML(谢美兰); Cui, Z(崔铮) | |
刊名 | JOURNAL OF MATERIALS CHEMISTRY C |
2015 | |
卷号 | 3期号:43页码:7 |
通讯作者 | Chen, Z (陈征) |
英文摘要 | Highly conductive indium tin oxide (ITO) nanocrystals and inks have been synthesized by solvothermal dehydration condensation of metal hydroxide in combination with in situ ethanolamine capping. It is found that the addition of ethanolamine can effectively reduce the size of nanocrystals and chemically modify their surfaces. The synthesized ITO nanocrystals can be well dispersed in ethanol with high solid content and the suspension is stable for days. Such a small-molecule capped ITO suspension has been used as a conductive ink to make transparent conductive films by spin coating. Furthermore, a water washing step has been introduced in the ITO film preparation process to improve their conductivity, resulting in a low resistivity of 8.9 x 10(-3) Omega cm after 2 hour annealing at 300 degrees C in a mixed Ar and H-2 atmosphere. |
收录类别 | SCI |
语种 | 英语 |
公开日期 | 2016-05-03 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinano.ac.cn/handle/332007/3454] |
专题 | 苏州纳米技术与纳米仿生研究所_印刷电子学部_崔铮团队 |
推荐引用方式 GB/T 7714 | Chen, Z,Qin, XC,Zhou, T,et al. Ethanolamine-assisted synthesis of size-controlled indium tin oxide nanoinks for low temperature solution deposited transparent conductive films[J]. JOURNAL OF MATERIALS CHEMISTRY C,2015,3(43):7. |
APA | Chen, Z.,Qin, XC.,Zhou, T.,Wu, XZ.,Shao, SS.,...&Cui, Z.(2015).Ethanolamine-assisted synthesis of size-controlled indium tin oxide nanoinks for low temperature solution deposited transparent conductive films.JOURNAL OF MATERIALS CHEMISTRY C,3(43),7. |
MLA | Chen, Z,et al."Ethanolamine-assisted synthesis of size-controlled indium tin oxide nanoinks for low temperature solution deposited transparent conductive films".JOURNAL OF MATERIALS CHEMISTRY C 3.43(2015):7. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论